Vol. 40, Issue 4, pp. 943-948 (2010)

Abstract

Eu²⁺-doped SrMg₂(PO₄)₂ phosphor with blue emission was prepared by the low temperature chemical solution process using inorganic salts as a starting material. Transparent sol was preheated at 300 °C for 120 min and then precursor was finally annealed at 900 °C for 240 min in a reducing CO atmosphere. Crystallinity, surface morphology and luminescent properties have been investigated. The phosphor emits bright blue luminescence with a peak wavelength at 423 nm under near-ultraviolet excitation at 363 nm.